| Product name | China Nickel Suppliers Ni200 Ni201 Nickel Sheet Plate for Battery Industry |
| Material | Ni200(N6), Ni201(N4) |
| Standard | ASTM B127/ASTM B162 |
| Specification | Thickness :0.025mm to 20mm |
| Width: 200mm to 1200mm | |
| Maximum Length: 3000mm | |
| Surface | Hot rolled/cold rolled |
| Delivery state | Cold Formed (Y)/ Half Hard (Y2)/ Soft (M) Payment Terms |
| Lead Time | L/C, T/T, Western Union, PayPal, Escrow |
| Package | Wooden case as outside, plastic bag as inside |
| Advantages of us | (1) CE and ISO9001-2008 certified |
| (2)SGS & BV Audited company | |
| (3) Third-party verification service provider | |
| (4) Most convenient transport & prompt delivery | |
| (5)Competitive price with best service | |
| (6) Industry experience over 10 years | |
| Product Feature | (1)Low Density and High Specification Strength |
| (2)Excellent Corrosion Resistance | |
| (3)Good resistance to effect of heat | |
| (4)Excellent Bearing to cryogenic property | |
| (5)Nonmagnetic and Non-toxic |
Characteristic and Differences
Nickel 200 is commercially pure wrought nickel. It is highly resistant to various reducing chemicals. It can also be used in oxidizing conditions that cause the formation of a passive oxide film, for instance its unexcelled resistance to caustic alkalis. Nickel 200 is limited to service at temperatures below 315℃, because at higher temperatures it suffers from graphitization which results in severely compromised properties. In that circumstance, Nickel 201 is used instead. It has a high Curietemperature and good magnetostrictive properties. Its thermal and electrical conductivities are higher than nickel alloys.
China Nickel Suppliers Ni200 Ni201 Nickel Sheet Plate for Battery Industry
Nickel 201 is the low-carbon version of Nickel 200. Because of its low carbon content, Nickel 201 is not subject to embrittlement by intergranularly precipitated carbon or graphite when exposed to temperatures of 315 to 760℃ for prolonged time if carbonaceous materials are not in contact with it. Therefore, it is a substitute for Nickel 200 in Applications above 315℃. However it does suffer from intergranular embrittlement by sulfur compounds at temperatures above 315℃. Sodium peroxide can be used to change them to sulfates to counteract their effect.
| Grade | Element Composition/% | |||||||
| Ni+Co | Mn | Cu | Fe | C | Si | Cr | S | |
| Ni201 | ≥99.0 | ≤0.35 | ≤0.25 | ≤0.30 | ≤0.02 | ≤0.3 | ≤0.2 | ≤0.01 |
| Ni200 | ≥99.0 | /≤0.35 | ≤0.25 | ≤0.30 | ≤0.15 | ≤0.3 | ≤0.2 | ≤0.01 |
| Grade | Density | Melting Point | Coefficient of expansion | Modulus of rigidity | Modulus of elasticity | Electrical resistivity |
| Ni200 | 8.9g/cm3 | 1455°C | 13.3 µm/m °C (20-100°C) | 81kN/mm2 | 204kN/mm2 | 9.6μW• cm |
| Ni201 | 1455°C | 13.1µm/m °C (20-100°C) | 82kN/mm2 | 207kN/mm2 | 8.5μW• cm | |
Electroplating, Aluminum Coloring: Its mechanical properties make it excellent for applications in the aerospace and defense industries and in moderately corrosive environments, such as
food processing equipment and chemical shipping drums. construction of the railroad, highway and so on,different kinds of mechanical equipment, electronics, battery, chemical processing, marine engineering
(1) For vacuum coating
(2) For making valves grid, inner components of valves
(3) For making lead, supporting wire
(4) High temperature components such as turbine blades, guide vanes, turbine disks.
(5) High pressure compressor disks,machine manufacturing and combustion chambers used in the manufacture of aviation, naval and industrial gas turbines
Finding a reliable supplier and ensuring
error-free production can be overwhelming.
As a leading sourcing company in China,
We have hundreds of experrts who can handle
the entire sourcing process from finding
suppliers to delivering products.